plastic mold steel
We must first know some of the basic injection mold knowledge before talking about plastic mold steel, first of all, the classification of plastic mold are generally is on the length of plastic mold by 5 grades, over a million times grade 1;grade 2:500,000-100 million;grade 3 :from 300,000 to 500,000;grade4:from 100,000 to 300,000, grade 5: 10 million below
Grade1 and 2 need mold stell hardness after heat-treatment reaching around HRC50 , or plastic which is easy to wear, could violate the tolerance, so we should select steel heat afetr treatment showing better performance, but also at high hardness of the state has good cutting performance, of course, There are other considerations. I seldom come into contact with Chinese-made plastic mold steel, it can only introduce commonly used in the Pearl River Delta for imported raw materials. Usually chosen in Sweden 8407, S136, U.S. 420, H13, Europe, 2316,2344,083, or Japan SKD61, DC53 (the original mold for the metal material, the use of special circumstances.) grade 1 steel. In addition, raw plastic materials and the added filler have a great impact on the mold steel choice, especially glass fiber could have a very strong worn impact on the mold cavity surface.
Some plastic materials have acid corrosion, and some added modified enhancer or other agent, such as glass fiber lead to mold damage, so plastic material selection should be considered. There is strong general election corrosive plastic S136, 2316,420 grade1 steel, then weak corrosive plastic should elect S136, 2316,420, there SKD61, NAK80, PAK90, 718M. Strong acid plastic material: PVC, POM, PBT plastic material weak acid has: PC, PP, PMMA, PA,
Product appearance of the requirements of the selection of plastic mold material there is also a great impact, transparent pieces and surface requirements of parabolic mirror products, may choose to use the material S136, 2316,718 S, NAK80, PAK90, 420, high transparency of the mold should choose S136 and 420.
More than meeting the product requirements are from the run, but as a designer, you not only can not be a good designer, you may have questions :are you involved in the demand for the cost of molds are re - Medium weight, you should also consider price, Take the S136 to compare with 2316, a difference of 55-60 yuan per kilogram, if you choose incorrectly, you may lose much money
3 Pre-hardened mold steel , there is grade: S136H, 2316H, 718H, 083H, hardness HB270 ---- 340, 45 die by P20, 718,738,618,2311,2711, particularly low for the requirements molds, may have used S50C, 45 # steel, that is, directly in the mold cavity up to do.
In addition, specific questions to specific treatment, flexibly adapt ,plastic moldingfor a designer is the basic requirement
steven cheng is the CEO of plastic mold www.sino-mould.com.cn and plastic molding www.plasticmoulds.net business with plastic mold engineer backgound and willing to discuss any topics as to the plastic industry.
Grade1 and 2 need mold stell hardness after heat-treatment reaching around HRC50 , or plastic which is easy to wear, could violate the tolerance, so we should select steel heat afetr treatment showing better performance, but also at high hardness of the state has good cutting performance, of course, There are other considerations. I seldom come into contact with Chinese-made plastic mold steel, it can only introduce commonly used in the Pearl River Delta for imported raw materials. Usually chosen in Sweden 8407, S136, U.S. 420, H13, Europe, 2316,2344,083, or Japan SKD61, DC53 (the original mold for the metal material, the use of special circumstances.) grade 1 steel. In addition, raw plastic materials and the added filler have a great impact on the mold steel choice, especially glass fiber could have a very strong worn impact on the mold cavity surface.
Some plastic materials have acid corrosion, and some added modified enhancer or other agent, such as glass fiber lead to mold damage, so plastic material selection should be considered. There is strong general election corrosive plastic S136, 2316,420 grade1 steel, then weak corrosive plastic should elect S136, 2316,420, there SKD61, NAK80, PAK90, 718M. Strong acid plastic material: PVC, POM, PBT plastic material weak acid has: PC, PP, PMMA, PA,
Product appearance of the requirements of the selection of plastic mold material there is also a great impact, transparent pieces and surface requirements of parabolic mirror products, may choose to use the material S136, 2316,718 S, NAK80, PAK90, 420, high transparency of the mold should choose S136 and 420.
More than meeting the product requirements are from the run, but as a designer, you not only can not be a good designer, you may have questions :are you involved in the demand for the cost of molds are re - Medium weight, you should also consider price, Take the S136 to compare with 2316, a difference of 55-60 yuan per kilogram, if you choose incorrectly, you may lose much money
3 Pre-hardened mold steel , there is grade: S136H, 2316H, 718H, 083H, hardness HB270 ---- 340, 45 die by P20, 718,738,618,2311,2711, particularly low for the requirements molds, may have used S50C, 45 # steel, that is, directly in the mold cavity up to do.
In addition, specific questions to specific treatment, flexibly adapt ,plastic moldingfor a designer is the basic requirement
steven cheng is the CEO of plastic mold www.sino-mould.com.cn and plastic molding www.plasticmoulds.net business with plastic mold engineer backgound and willing to discuss any topics as to the plastic industry.